Silk fibres exhibiting biodegradability & superhydrophobicity for recovery of petroleum oils from oily wastewater.

Present study reports superhydrophobic-oleophilic, environment-friendly, & biodegradable silk material derived from Bombyx mori silkworm, for practical oil-water separation and oil recovery applications. In this study, raw silk fibers were degummed using water and Na₂CO₃ (at 100 °C), for removal of outer gummy sericin protein layer, which was confirmed using FTIR & FE-SEM analysis. The water & Na₂CO₃ degummed silk fibers showed superhydrophobicity with water contact angles (WCA) of 153° & 158°, respectively, demonstrating Wenzel & Cassi-Baxter states. Degummed silk fibers showed superoleophilicity (OCA∼0°) towards petroleum oils like Petrol, Diesel, & Engine oil. The water & Na₂CO₃ degummed silk fibers showed oil-water separation efficiencies of 95 % & 87.5 %, respectively. Both degummed silk fibers showed more than 50 % efficiency till 10 separation cycles. Further, raw & degummed silk fibers showed an environmental biocompatibility, by their biodegradation under in-house developed biotic de-compost culture consisting of biodegrading micro-organisms. Their analysis showed that biotic de-compost culture rendered biodegradation weight loss of 11 % and 18 %, respectively, in 35 days. Successive results showed that, degummed silk fibers can be effectively utilized for practical oil-water separation, and further, they can be environmentally biodegraded, thereby mitigating their waste generation and disposal problem.