Citric acid functionalized silane coupling versus post-grafting strategy for dual pH and saline responsive delivery of cisplatin by Fe3O4/carboxyl functionalized mesoporous SiO2 hybrid nanoparticles: A-synthesis, physicochemical and biological characterization.

Synthesis of monodisperse carboxylic acid-functionalized magnetic mesoporous silica nanoparticles is performed by either two-step sol-gel process or post-grafting using citric acid modified isocyanate silane coupling agent (MMSN-NCO-CA) or succinic anhydride modified magnetic mesoporous silica (MMSN-NH-SA). Morphology, structure and magnetic properties of bare and mesoporous silica coated Fe₃O₄ core were studied using various techniques such as FTIR, VSM, TEM, FESEM, XRD and N₂ adsorption-desorption isotherms (BET). Cisplatin (cis-Pt) adsorption isotherms and its release profile in various media were investigated by ICP-OES. MMSN-NCO-CA with mean particle size 107 nm had lower surface area (87.5 m²/g) and larger pore size (6.9 nm) in comparison with MMSN-NH-SA (respective values of 151.2 m²/g and 3.5 nm). cis-Pt loading into particles followed a saturable adsorption with respect to the drug to particle mass ratios. More sustained release of cis-Pt was observed for MMSN-NCO-CA, though both nanoparticles exhibited a pH- and saline concentration-dependent drug release. In addition, general and cis-Pt specific cytotoxicity were examined by MTT assay in MDA-MB-231 breast cancer cell line, and to further detect apoptosis, acridine orange/ethidium bromide dual cell staining was investigated by fluorescence microscopy. In-vitro anti-tumor efficiency of cis-Pt loaded MMSN-NCO-CA and MMSN-NH-SA were similarly enhanced in comparison to free cis-Pt; however, more specific apoptotic death occurred for cis-Pt loaded MMSN-NCO-CA. Therefore, the as-synthesized citric acid functionalized core-shell magnetic mesoporous hybrid nanoparticles could be used as a promising drug carriers for cancer therapy in-vivo.