Fatigue performance of fully-stabilized zirconia polycrystals monolithic restorations: The effects of surface treatments at the bonding surface

This study evaluated the distinct conditioning effect of the intaglio surface of bonded fully-stabilized zirconia (FSZ) simplified restorations on the mechanical fatigue behavior of the set prior to and after aging. Ceramic disc shaped specimens (Ø= 10 mm and 1 mm thick) were randomly allocated into 14 groups considering: "surface treatments" (Ctrl: no-treatment; PM: universal primer; GLZ: low-fusing porcelain glaze; SNF: 5 nm SiO₂ nanofilm deposition; AlOx: air-abrasion with aluminum oxide; SiC: air-abrasion with silica-coated aluminum oxide; 7%Si: air-abrasion with 7% silica-coated aluminum oxide); and "aging" (baseline: 24 h at 37 °C in water; or aged: 90 days at 37 °C in water + 12,000 thermal cycles). The discs were treated, luted with resin cement onto the dentin analog, subjected to aging or not, and then tested under a step-stress fatigue test at 20 Hz, 10,000 cycles/step, step-size of 100N starting at 200N, and proceeding until failure detection. Fractographic, topographic, surface roughness, contact angle, and atomic force microscopy analyzes were performed. The surface treatments at baseline led to statistically similar fatigue failure loads (953N-1313N), except for GLZ (1313N), which was significantly higher than 7%Si (953 N). Meanwhile, Ctrl had 40% pre-test failures (debonding) after aging, and therefore the worst fatigue performance (notable decrease in fatigue results), while all the other groups presented superior and statistically similar fatigue behavior (973-1271N). In fact, when considering baseline Vs aging conditions, stable fatigue results could only be noted when using surface treatments. In conclusion, internal surface treatments of FSZ ceramic restorations are mandatory for fatigue behavior stability after aging the restorative set, while non-treatment induced unstable results.

Keywords: Fatigue phenomena; Surface characteristics; Surface treatments to enhance adhesion; Survival analysis; Yttrium stabilized zirconia polycrystals.