An estimation of fatigue life for a carbon fibre/poly ether ether ketone hip joint prosthesis.
Ключови думи
Резюме
A fracture mechanics approach was applied to estimate the life of a prosthesis injection moulded from short carbon fibre reinforced poly ether ether ketone. Flexural modulus and strength, fracture toughness, fatigue endurance limit, fatigue crack growth rate and threshold stress intensity factor were determined. The dimensions of the test pieces were selected to yield fibre orientation and fibre length distributions similar to those obtained in the prosthesis. Stress levels generated in the prosthesis under different activities were estimated by conducting three-dimensional finite element analysis. It was shown by a fracture mechanics approach that a fatigue failure due to the propagation of an embedded elliptical slit, under these stresses, would be unlikely for a crack length smaller than 1.85 mm. However, the cement would fail under the same conditions, irrespective of the type of the prosthesis employed.