Deutsch
Albanian
Arabic
Armenian
Azerbaijani
Belarusian
Bengali
Bosnian
Catalan
Czech
Danish
Deutsch
Dutch
English
Estonian
Finnish
Français
Greek
Haitian Creole
Hebrew
Hindi
Hungarian
Icelandic
Indonesian
Irish
Italian
Japanese
Korean
Latvian
Lithuanian
Macedonian
Mongolian
Norwegian
Persian
Polish
Portuguese
Romanian
Russian
Serbian
Slovak
Slovenian
Spanish
Swahili
Swedish
Turkish
Ukrainian
Vietnamese
Български
中文(简体)
中文(繁體)
Clinical Oral Investigations 2001-Dec

Effect of surface treatment on fatigue behaviour between Tetric Ceram inlays and Variolink luting composite.

Nur registrierte Benutzer können Artikel übersetzen
Einloggen Anmelden
Der Link wird in der Zwischenablage gespeichert
R Frankenberger
W O Strobel
J Baresel
T Trapper
N Krämer
A Petschelt

Schlüsselwörter

Abstrakt

The effect of pre-treatment of composite inlays on bonding performance between a resin composite inlay and a luting composite has not been fully studied. The aim of the present study was to evaluate the influence of three different pre-treatment modes on fatigue bond strength and marginal adaptation. One hundred twenty resin composite discs (Tetric Ceram) were made as simulated inlays and randomly assigned to four groups (n=30): Without treatment (WT), hydrofluoric acid etching for 15 s + silanating (HF), roughening with a silicon carbide bur (SC), and silica coating + silanating (CO). Luting composite cylinders (Variolink II low) were bonded to the discs using Heliobond, and after 24 h in water at 37 degrees C, quasistatic shear bond strengths (n=l) and fatigue bond strengths (n=20; 5,000 cycles) were measured. Thirty-two third molars received occlusomesial Class II cavities (n=8), and direct resin composite inlays were luted with identical methods and materials. Before and after thermomechanical loading (100,000x50 N, 2,500 x +5 degrees C/+55 degrees C), replicas were made and examined (SEM, x200). CO and SC exhibited significantly higher bond strengths and adhesive fatigue limits than HF and WT (P<0.05). After thermomechanical loading, CO (98% continuous margin) and SC (95% continuous margin) demonstrated that they provide significantly more fatigue resistance than HF (88%).

Treten Sie unserer
Facebook-Seite bei

Die vollständigste Datenbank für Heilkräuter, die von der Wissenschaft unterstützt wird

  • Arbeitet in 55 Sprachen
  • Von der Wissenschaft unterstützte Kräuterkuren
  • Kräutererkennung durch Bild
  • Interaktive GPS-Karte - Kräuter vor Ort markieren (in Kürze)
  • Lesen Sie wissenschaftliche Veröffentlichungen zu Ihrer Suche
  • Suchen Sie nach Heilkräutern nach ihrer Wirkung
  • Organisieren Sie Ihre Interessen und bleiben Sie über Neuigkeiten, klinische Studien und Patente auf dem Laufenden

Geben Sie ein Symptom oder eine Krankheit ein und lesen Sie über Kräuter, die helfen könnten, geben Sie ein Kraut ein und sehen Sie Krankheiten und Symptome, gegen die es angewendet wird.
* Alle Informationen basieren auf veröffentlichten wissenschaftlichen Forschungsergebnissen

Google Play badgeApp Store badge