New Concept of Polymethyl Methacrylate (PMMA) and Polyethylene Terephthalate (PET) Surface Coating by Chitosan.

Chitosan is known for its hemostatic and antimicrobial properties and might be useful for temporary coating of removable dentures or intraoral splints to control bleeding after oral surgery or as a supportive treatment in denture stomatitis. This study investigated a new method to adhere chitosan to polymethyl methacrylate (PMMA) and polyethylene terephthalate (PET). There were 70 cylindrical specimens made from PMMA and 70 from PET (13 mm diameter, 6 mm thickness). The materials with ten specimens each were sandblasted at 2.8 or 4.0 bar with aluminum oxide 110 μm or/and aluminum oxide coated with silica. After sandblasting, all specimens were coated with a 2% or 4% acetic chitosan solution with a thickness of 1 mm. Then the specimens were dried for 120 min at 45 °C. The precipitated chitosan was neutralized with 1 mol NaOH. After neutralization, all specimens underwent abrasion tests using the tooth-brushing simulator with soft brushes (load 2N, 2 cycles/s, 32 °C, 3000 and 30,000 cycles). After each run, the specimen surfaces were analyzed for areas of remaining chitosan by digital planimetry under a light microscope. The best chitosan adhesion was found after sandblasting with aluminum oxide coated with silica (U-Test, p < 0.05) in both the PMMA and the PET groups. Hence, with relatively simple technology, a reliable bond of chitosan to PMMA and PET could be achieved.