Synergistic Effects of Stress-Rupture and Cyclic Loading on Strain Response of Fiber-Reinforced Ceramic-Matrix Composites at Elevated Temperature in Oxidizing Atmosphere.

In this paper, the synergistic effects of stress rupture and cyclic loading on the strain response of fiber-reinforced ceramic-matrix composites (CMCs) at elevated temperature in air have been investigated. The stress-strain relationships considering interface wear and interface oxidation in the interface debonded region under stress rupture and cyclic loading have been developed to establish the relationship between the peak strain, the interface debonded length, the interface oxidation length and the interface slip lengths. The effects of the stress rupture time, stress levels, matrix crack spacing, fiber volume fraction and oxidation temperature on the peak strain and the interface slip lengths have been investigated. The experimental fatigue hysteresis loops, interface slip lengths, peak strain and interface oxidation length of cross-ply SiC/MAS (magnesium alumino-silicate, MAS) composite under cyclic fatigue and stress rupture at 566 and 1093 °C in air have been predicted.