Bio-redox potential of Hyphaene thebaica in bio-fabrication of ultrafine maghemite phase iron oxide nanoparticles (Fe2O3 NPs) for therapeutic applications.

Maghemite (Fe₂O₃-NPs) nanoparticles were synthesized by a convenient, green and cost effective method using aqueous fruit extracts of Hyphaene thebaica. Different techniques like FTIR, XRD, UV-Vis, Raman, HR-TEM, EDS. SAED, Zeta potential were used to establish the nature of Fe₂O₃-NPs, while the therapeutic properties were studied using different biological assays including antiviral, antibacterial, antifungal, antioxidant and enzyme inhibition assays. XRD pattern revealed sharp peaks and a crystalline nature of Fe₂O₃-NPs. HR-TEM revealed quasi-spherical and cuboidal morphologies, while the particle size in ~10 nm. FTIR indicated a sharp peak centered at ~444 cm^-1 which is the characteristic FeO band vibration. SAED pattern indicated the crystalline nature while EDS also confirmed the synthesis of Fe₂O₃ NPs. Zeta potential was obtained in different solvents and physiological buffers indicating highest value in water (-26.5 mV) and lowest in DMSO (-15.8 mV). Tested bacterial strains, Bacillus subtilis was found to be inhibited significantly. Aspergillus flavus appeared to be susceptible to all of the tested concentration of Fe₂O₃ NPs. Maximum 40.78% FRSA was obtained at 400 μg/mL. Cell culture based studies on RD cells and L20B cells indicated reduction in viability of cells with increase concentration of Fe₂O₃ NPs. Moderate inhibition of polio virus-1 and polio virus-2 was observed, after culturing the virus in the L20B cells. Excellent Protein Kinase (PK) inhibition was revealed. Hemolytic potential and cytotoxic potential was indicated to be dose dependent. In conclusion, the present report for the first time reports the synthesis of Fe₂O₃ NPs from H. thebaica fruits and reveals their biomedical potential including antiviral potential.