Surface Characterization, Antimicrobial Activity, and Biocompatibility of Autopolymerizing Acrylic Resins Coated with Reynoutria elliptica Extract

We conducted surface characterization to assess the biocompatibility and investigate the antimicrobial activity against oral pathogens in autopolymerizing acrylic resins, coated with light-curable coating resin, containing various concentrations of Reynoutria elliptica extract (0, 200, 400, and 600 µg/mL). The R. elliptica extract powder was prepared using a freeze-drying technique. Further, a goniometer and microhardness tester were used to determine the water contact angle, and Vickers hardness, respectively; color measurements were performed on the uncoated and coated acrylic resin disks. The polyphenol content of the extracts from the coated acrylic resin disk was analyzed using UV-VIS spectroscopy. The antimicrobial activity of the coated acrylic resin disk against Streptococcus mutans and Candida albicans was observed for 24 and 48 h by measuring the optical density using spectrophotometry. In addition, biocompatibility was confirmed by testing the cell viability according to ISO 10993-5. The water contact angle, Vickers hardness, and color change values of the coated acrylic resin disks were not significantly different from the control. Polyphenol was detected in all experimental groups, with no significant differences between the experimental groups. The experimental groups exhibited significant antimicrobial activity against S. mutans and C. albicans compared to the control group, after 48 h of incubation. The cell viability between the control and experimental groups was not significantly different. The proposed coating resin containing R. elliptica extract is applicable on dental acrylic resins, due to their antimicrobial properties and excellent biocompatibility, with no deterioration of surface characteristics.

Keywords: Reynoutria elliptica extract; antimicrobial activity; cell viability; coating resin; contact angle; microhardness; polyphenol.