Bond strength and elemental analysis of oxidized dentin bonded to resin modified glass ionomer based restorative material.

This study aimed to investigate the influence of hesperidin application on the bonding of resin-modified glass ionomer-based restorative material to dentin treated with oxygen-induced endodontic irrigants.One hundred human permanent molars were categorized into five groups (n= 20/group), treated with various irrigants as follows: Group C; distilled water (control group), Group SH; 5.25% NaOCl, Group SH+H; 5.25% NaOCl + 5 % hesperidin, Group HP; 10% H2O2, Group HP+H; 10% H2O2 + 5 % hesperidin. Specimens were bonded with RMGI based restorative material. For each group, half of the specimens were evaluated for µSBS by a universal testing machine and the other half for dentin ion uptake by EDX. Additional ten specimens (n=2/per group) were prepared for the micro-morphological analysis under SEM.

Hesperidin groups improved the µSBS, with a significant effect for HP+H group (p<. 05). Dentin ion uptake was significantly (p<. 05) improved in hesperidin groups.

In conclusion, Application of hesperidin in conjunction with RMGI based restorative material improved the dentin bond strength and ion uptake; this could be a promising approach to aid dental practitioners in their decisions, regarding which restorative material to use especially in caries susceptible patients. Key words:Hesperidin, elemental analysis, bond strength.